Sintering of Fly Ash Based Composites with Zeolite and Bentonite Addition for Application in Construction Materials
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Due to pozzolanic characteristics, fly ash is commonly used as a cement replacement in construction composites. Addition of natural clays with sorption ability (i.e. zeolite and bentonite) in to the fly ash based construction ...
Characterization of MgAl2O4 sintered ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
Single phase MgAl2O4 was made from a one-to-one molar ratio of MgO and Al2O3 powders mixed using ball-milling. Mixtures of MgO and Al2O3 were subsequently treated in planetary ball mill for 30, 60, 90 and 120 minutes in ...
The influence of alumino-silicate matrix composition on surface hydrophobic properties
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
The purpose of this investigation is to investigate the hydrophobicity of geopolymers, new alumino-silicate materials and the influence of Si/Al ratio on their surface properties. Contact angle measurement (CAM) as reliable ...
Electrical Properties of Magnesium Titanate Ceramics Post-Sintered by Hot Isostatic Pressing
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Post-sintering of magnesium titanate ceramics by hot isostatic pressing (HIP) in an oxygen-free atmosphere significantly alters various electrical properties of the product. In particular, the sintered material becomes a ...
Characterisation of Mn0.63Zn0.37Fe2O4 Powders After Intensive Milling and Subsequent Thermal Treatment
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes ...
Physical Properties of Sintered Alumina Doped with Different Oxides
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2018)
Corundum (alpha-alumina) is a suiTab. material for usage in various industry fields owing to its chemical stability, electrical and mechanical features. It is known that properties of ceramics could be modified by addition ...
Characterization of FeCoV Alloy Processed by PIM/MIM Route
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
In this study the characterization of FeCo-2V alloys toroidal samples produced by PIM/MIM technology was presented. The feedstock for metal injection molding (MIM) was prepared by mixing starting FeCoV powder with a low ...
Analysis of the initial-stage sintering of mechanically activated SrTiO3
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
The initial-stage of sintering plays a significant role in determining the final microstructure that defines the main characteristics of electroceramics materials such as functional properties. In this article non-isothermal ...
Formation of Porous Wollastonite-based Ceramics after Sintering With Yeast as the Pore-forming Agent
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
In this paper, synthesis of porous wollastonite-based ceramics was reported. Ceramic precursor, methylhydrocyclosiloxane, together with micro-sized CaCO3, was used as starting material. After 20 min of ultrasound treatment, ...
Microstructure and Phase Composition Of Steatite Ceramics Sintered by Traditional and Spark Plasma Sintering
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2018)
The influence of the sintering method on the mineral phase transformations and development of the crystalline microstructure of steatite ceramics was investigated. The steatite samples were fabricated from talc and bentonite ...