Synthesis of Barium-zinc-titanate Ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2012)
Mixtures of BaCO3, ZnO and TiO2 powders, with molar ratio of 1:2:4, were mechanically activated for 20, 40 and minutes in a planetary ball mill. The resulting powders were compacted into pellets and isothermally sintered ...
Mechanical-Chemical Synthesis Ba0.77Sr0.23TiO3
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2012)
Barium-Strontium-Titanate Ba0.77Sr0.23TiO3 was prepared from starting materials BaCO3, SrCO3 and TiO2 through solid-state reactions. Mixtures of these oxides are mechanically activated in a high-energy planetary ball mill ...
Sintering Process Influence on Microstructure and Intergranular Impedance of Rare-Earth Modified BaTiO3-Ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2011)
Sintering process is a complex of different synergetic effects during the ceramics materials consolidation. The microstructural level properties control is very important as a stage in advanced materials prognosis. SEM ...
Electrical Properties and Microstructure Fractal Analysis of Magnesium-Modified Aluminium-Silicate Ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2011)
The addition of Mg(2)(NO)(3) and some active additives, composed of Al salts, to the mixtures of kaolinite and bentonite can provide clay compositions which, after sintering at high temperatures, produce very porous ceramics ...
Isothermal kinetics of titanium-oxo-alkoxy clusters formation
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2011)
In this article, the influences of titanium tetraisopropoxide Ti(OR)4 (R = Pri) concentration, molar ratio, h = [H2O]/[Ti(OR)4], and temperature, on the formation kinetics of the titanium-oxo-alkoxy clusters (TOAC), were ...
Analysis and Modeling of Sintering of Sr-hexaferrite Produced by PIM Technology
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2011)
The powder injection moulding (PIM) technology is lately becoming more and more significant due to complex design possibilities and good repeatability. This technology requires optimization of all steps starting with ...
Sintering of Mechanically Activated Magnesium-titanate and Barium-zinc-titanate Ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2011)
In this article the influence of mechanical activation on sintering process of magnesium-titanate and barium-zinc-titanate ceramics has been investigated. Both non-activated and mixtures treated in planetary ball mill for ...
Physical Properties of Sintered Alumina Doped with Different Oxides
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2018)
Corundum (alpha-alumina) is a suiTab. material for usage in various industry fields owing to its chemical stability, electrical and mechanical features. It is known that properties of ceramics could be modified by addition ...
Characterisation of Mn0.63Zn0.37Fe2O4 Powders After Intensive Milling and Subsequent Thermal Treatment
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes ...
Analysis of early-stage sintering mechanisms of mechanically activated BaTiO3
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Barium-titanate powder was mechanically activated in a planetary-ball mill for 60 and 120 minutes. Non-isothermal sintering of non-activated and activated powder samples was investigated using a dilatometer in the temperature ...