Influence of alloyed layer (FeSn2) and porosity of stannic sheathing on the corrosion of tinned sheet-iron
Uticaj zalegiranog sloja (FeSn2) i poroznosti kalajne prevlake na koroziju belog lima
Apstrakt
Depending on the type of black sheet-iron pickling, with the acid sulphate (H2SO4) or sodium sulphate (Na2SO4), before electrolitic drifting of tin, at the production of tinned sheet-irons it was examined morphology of alloyed layer of FeSn2 using SEM microscope and diffraction of X-rays (X-RD). Supposed weight of tin is measured by EDAX analysis. Porosity of the surface was determined by ASTM specification and by potenciostic polarisation. Resistance on corrosion was measured through the ATC test, methods and AC impedance. Achieved results indicates on big importance of pickling type of white sheet-iron at his process of production.
U zavisnosti od tipa dekapiranja crnog lima, sa sumpornom kiselinom (H2SO4) ili natrijumsulfatom (Na2SO4), pre elektrolitičkog nanošenja kalaja, kod proizvodnje belih limova, ispitivana je morfologija zalegiranog sloja FeSn2 pomoću SEM mikroskopa i difrakcije rendgen zraka (X-RD). Prividna težina kalaja je merena EDAX analizom. Poroznost površine je određivana ASTM specifikacijom i potenciostatskom polarizacijom. Otpornost na koroziju je ocenjena preko ATC testa, potenciostatskih metoda i metode AC impedance. Dobijeni rezultati ukazuju na veliku važnost tipa dekapiranja belog lima u njegovom procesu proizvodnje.
Izvor:
Zbornik radova Tehnološkog fakulteta, Leskovac, 2005, 15, 58-72Izdavač:
- Univerzitet u Nišu - Tehnološki fakultet, Leskovac
Institucija/grupa
Poljoprivredni fakultetTY - JOUR AU - Tošković, D. AU - Rajković, Miloš AU - Vasiljević, Ljubica AU - Stanojević, Dušan D. PY - 2005 UR - http://aspace.agrif.bg.ac.rs/handle/123456789/932 AB - Depending on the type of black sheet-iron pickling, with the acid sulphate (H2SO4) or sodium sulphate (Na2SO4), before electrolitic drifting of tin, at the production of tinned sheet-irons it was examined morphology of alloyed layer of FeSn2 using SEM microscope and diffraction of X-rays (X-RD). Supposed weight of tin is measured by EDAX analysis. Porosity of the surface was determined by ASTM specification and by potenciostic polarisation. Resistance on corrosion was measured through the ATC test, methods and AC impedance. Achieved results indicates on big importance of pickling type of white sheet-iron at his process of production. AB - U zavisnosti od tipa dekapiranja crnog lima, sa sumpornom kiselinom (H2SO4) ili natrijumsulfatom (Na2SO4), pre elektrolitičkog nanošenja kalaja, kod proizvodnje belih limova, ispitivana je morfologija zalegiranog sloja FeSn2 pomoću SEM mikroskopa i difrakcije rendgen zraka (X-RD). Prividna težina kalaja je merena EDAX analizom. Poroznost površine je određivana ASTM specifikacijom i potenciostatskom polarizacijom. Otpornost na koroziju je ocenjena preko ATC testa, potenciostatskih metoda i metode AC impedance. Dobijeni rezultati ukazuju na veliku važnost tipa dekapiranja belog lima u njegovom procesu proizvodnje. PB - Univerzitet u Nišu - Tehnološki fakultet, Leskovac T2 - Zbornik radova Tehnološkog fakulteta, Leskovac T1 - Influence of alloyed layer (FeSn2) and porosity of stannic sheathing on the corrosion of tinned sheet-iron T1 - Uticaj zalegiranog sloja (FeSn2) i poroznosti kalajne prevlake na koroziju belog lima EP - 72 IS - 15 SP - 58 UR - https://hdl.handle.net/21.15107/rcub_agrospace_932 ER -
@article{ author = "Tošković, D. and Rajković, Miloš and Vasiljević, Ljubica and Stanojević, Dušan D.", year = "2005", abstract = "Depending on the type of black sheet-iron pickling, with the acid sulphate (H2SO4) or sodium sulphate (Na2SO4), before electrolitic drifting of tin, at the production of tinned sheet-irons it was examined morphology of alloyed layer of FeSn2 using SEM microscope and diffraction of X-rays (X-RD). Supposed weight of tin is measured by EDAX analysis. Porosity of the surface was determined by ASTM specification and by potenciostic polarisation. Resistance on corrosion was measured through the ATC test, methods and AC impedance. Achieved results indicates on big importance of pickling type of white sheet-iron at his process of production., U zavisnosti od tipa dekapiranja crnog lima, sa sumpornom kiselinom (H2SO4) ili natrijumsulfatom (Na2SO4), pre elektrolitičkog nanošenja kalaja, kod proizvodnje belih limova, ispitivana je morfologija zalegiranog sloja FeSn2 pomoću SEM mikroskopa i difrakcije rendgen zraka (X-RD). Prividna težina kalaja je merena EDAX analizom. Poroznost površine je određivana ASTM specifikacijom i potenciostatskom polarizacijom. Otpornost na koroziju je ocenjena preko ATC testa, potenciostatskih metoda i metode AC impedance. Dobijeni rezultati ukazuju na veliku važnost tipa dekapiranja belog lima u njegovom procesu proizvodnje.", publisher = "Univerzitet u Nišu - Tehnološki fakultet, Leskovac", journal = "Zbornik radova Tehnološkog fakulteta, Leskovac", title = "Influence of alloyed layer (FeSn2) and porosity of stannic sheathing on the corrosion of tinned sheet-iron, Uticaj zalegiranog sloja (FeSn2) i poroznosti kalajne prevlake na koroziju belog lima", pages = "72-58", number = "15", url = "https://hdl.handle.net/21.15107/rcub_agrospace_932" }
Tošković, D., Rajković, M., Vasiljević, L.,& Stanojević, D. D.. (2005). Influence of alloyed layer (FeSn2) and porosity of stannic sheathing on the corrosion of tinned sheet-iron. in Zbornik radova Tehnološkog fakulteta, Leskovac Univerzitet u Nišu - Tehnološki fakultet, Leskovac.(15), 58-72. https://hdl.handle.net/21.15107/rcub_agrospace_932
Tošković D, Rajković M, Vasiljević L, Stanojević DD. Influence of alloyed layer (FeSn2) and porosity of stannic sheathing on the corrosion of tinned sheet-iron. in Zbornik radova Tehnološkog fakulteta, Leskovac. 2005;(15):58-72. https://hdl.handle.net/21.15107/rcub_agrospace_932 .
Tošković, D., Rajković, Miloš, Vasiljević, Ljubica, Stanojević, Dušan D., "Influence of alloyed layer (FeSn2) and porosity of stannic sheathing on the corrosion of tinned sheet-iron" in Zbornik radova Tehnološkog fakulteta, Leskovac, no. 15 (2005):58-72, https://hdl.handle.net/21.15107/rcub_agrospace_932 .