Mixtures of BaCO3, ZnO and TiO2 powders, with molar ratio of 1:2:4, were mechanically activated for 20, 40 and minutes in a planetary ball mill. The resulting powders were compacted into pellets and isothermally sintered at 1250 degrees C for 2h with a heating rate of 10 degrees C/min. X-ray diffraction analysis of obtained powders and sintered samples was performed in order to investigate changes of the phase composition. The microstructure of sintered samples was examined by scanning electron microscopy. The photoacoustic phase and amplitude spectra of sintered samples were measured as a function of the laser beam modulating frequency using a transmission detection configuration. Fitting of experimental data enabled determination of photoacoustic properties including thermal diffusivity. Based on the results obtained correlation between thermal diffusivity and experimental conditions, as well the samples microstructure characteristics, was discussed.
TY - JOUR
AU - Obradović, N.
AU - Nikolić, M.V.
AU - Nikolić, N.
AU - Filipović, Suzana
AU - Mitrić, M.
AU - Pavlović, Vladimir
AU - Nikolić, P.M.
AU - Djordjević, Antonije
AU - Ristić, M.M.
PY - 2012
UR - http://aspace.agrif.bg.ac.rs/handle/123456789/3052
AB - Mixtures of BaCO3, ZnO and TiO2 powders, with molar ratio of 1:2:4, were mechanically activated for 20, 40 and minutes in a planetary ball mill. The resulting powders were compacted into pellets and isothermally sintered at 1250 degrees C for 2h with a heating rate of 10 degrees C/min. X-ray diffraction analysis of obtained powders and sintered samples was performed in order to investigate changes of the phase composition. The microstructure of sintered samples was examined by scanning electron microscopy. The photoacoustic phase and amplitude spectra of sintered samples were measured as a function of the laser beam modulating frequency using a transmission detection configuration. Fitting of experimental data enabled determination of photoacoustic properties including thermal diffusivity. Based on the results obtained correlation between thermal diffusivity and experimental conditions, as well the samples microstructure characteristics, was discussed.
PB - Međunarodni Institut za nauku o sinterovanju, Beograd
T2 - Science of Sintering
T1 - Synthesis of Barium-zinc-titanate Ceramics
EP - 71
IS - 1
SP - 65
VL - 44
DO - 10.2298/SOS1201065O
ER -
@article{
author = "Obradović, N. and Nikolić, M.V. and Nikolić, N. and Filipović, Suzana and Mitrić, M. and Pavlović, Vladimir and Nikolić, P.M. and Djordjević, Antonije and Ristić, M.M.",
year = "2012",
abstract = "Mixtures of BaCO3, ZnO and TiO2 powders, with molar ratio of 1:2:4, were mechanically activated for 20, 40 and minutes in a planetary ball mill. The resulting powders were compacted into pellets and isothermally sintered at 1250 degrees C for 2h with a heating rate of 10 degrees C/min. X-ray diffraction analysis of obtained powders and sintered samples was performed in order to investigate changes of the phase composition. The microstructure of sintered samples was examined by scanning electron microscopy. The photoacoustic phase and amplitude spectra of sintered samples were measured as a function of the laser beam modulating frequency using a transmission detection configuration. Fitting of experimental data enabled determination of photoacoustic properties including thermal diffusivity. Based on the results obtained correlation between thermal diffusivity and experimental conditions, as well the samples microstructure characteristics, was discussed.",
publisher = "Međunarodni Institut za nauku o sinterovanju, Beograd",
journal = "Science of Sintering",
title = "Synthesis of Barium-zinc-titanate Ceramics",
pages = "71-65",
number = "1",
volume = "44",
doi = "10.2298/SOS1201065O"
}
Obradović, N., Nikolić, M.V., Nikolić, N., Filipović, S., Mitrić, M., Pavlović, V., Nikolić, P.M., Djordjević, A.,& Ristić, M.M.. (2012). Synthesis of Barium-zinc-titanate Ceramics. in Science of Sintering
Međunarodni Institut za nauku o sinterovanju, Beograd., 44(1), 65-71.
https://doi.org/10.2298/SOS1201065O
Obradović N, Nikolić M, Nikolić N, Filipović S, Mitrić M, Pavlović V, Nikolić P, Djordjević A, Ristić M. Synthesis of Barium-zinc-titanate Ceramics. in Science of Sintering. 2012;44(1):65-71.
doi:10.2298/SOS1201065O .
Obradović, N., Nikolić, M.V., Nikolić, N., Filipović, Suzana, Mitrić, M., Pavlović, Vladimir, Nikolić, P.M., Djordjević, Antonije, Ristić, M.M., "Synthesis of Barium-zinc-titanate Ceramics" in Science of Sintering, 44, no. 1 (2012):65-71,
https://doi.org/10.2298/SOS1201065O . .