Synthesis of Barium-zinc-titanate Ceramics

2012
Аутори
Obradović, N.
Nikolić, M.V.
Nikolić, N.
Filipović, Suzana

Mitrić, M.

Pavlović, Vladimir

Nikolić, P.M.
Djordjević, Antonije
Ristić, M.M.
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
Mixtures of BaCO3, ZnO and TiO2 powders, with molar ratio of 1:2:4, were mechanically activated for 20, 40 and minutes in a planetary ball mill. The resulting powders were compacted into pellets and isothermally sintered at 1250 degrees C for 2h with a heating rate of 10 degrees C/min. X-ray diffraction analysis of obtained powders and sintered samples was performed in order to investigate changes of the phase composition. The microstructure of sintered samples was examined by scanning electron microscopy. The photoacoustic phase and amplitude spectra of sintered samples were measured as a function of the laser beam modulating frequency using a transmission detection configuration. Fitting of experimental data enabled determination of photoacoustic properties including thermal diffusivity. Based on the results obtained correlation between thermal diffusivity and experimental conditions, as well the samples microstructure characteristics, was discussed.
Кључне речи:
Ceramics / Mechanochemical processing / Sintering / X-ray diffractionИзвор:
Science of Sintering, 2012, 44, 1, 65-71Издавач:
- Međunarodni Institut za nauku o sinterovanju, Beograd
Финансирање / пројекти:
- Serbian Academy of Sciences and Arts [F-198]
- Усмерена синтеза, структура и својства мултифункционалних материјала (RS-172057)
- 0-3D наноструктуре за примену у електроници и обновљивим изворима енергије: синтеза, карактеризација и процесирање (RS-45007)
DOI: 10.2298/SOS1201065O
ISSN: 0350-820X
WoS: 000318147700007
Scopus: 2-s2.0-84864298816
Институција/група
Poljoprivredni fakultetTY - JOUR AU - Obradović, N. AU - Nikolić, M.V. AU - Nikolić, N. AU - Filipović, Suzana AU - Mitrić, M. AU - Pavlović, Vladimir AU - Nikolić, P.M. AU - Djordjević, Antonije AU - Ristić, M.M. PY - 2012 UR - http://aspace.agrif.bg.ac.rs/handle/123456789/3052 AB - Mixtures of BaCO3, ZnO and TiO2 powders, with molar ratio of 1:2:4, were mechanically activated for 20, 40 and minutes in a planetary ball mill. The resulting powders were compacted into pellets and isothermally sintered at 1250 degrees C for 2h with a heating rate of 10 degrees C/min. X-ray diffraction analysis of obtained powders and sintered samples was performed in order to investigate changes of the phase composition. The microstructure of sintered samples was examined by scanning electron microscopy. The photoacoustic phase and amplitude spectra of sintered samples were measured as a function of the laser beam modulating frequency using a transmission detection configuration. Fitting of experimental data enabled determination of photoacoustic properties including thermal diffusivity. Based on the results obtained correlation between thermal diffusivity and experimental conditions, as well the samples microstructure characteristics, was discussed. PB - Međunarodni Institut za nauku o sinterovanju, Beograd T2 - Science of Sintering T1 - Synthesis of Barium-zinc-titanate Ceramics EP - 71 IS - 1 SP - 65 VL - 44 DO - 10.2298/SOS1201065O ER -
@article{ author = "Obradović, N. and Nikolić, M.V. and Nikolić, N. and Filipović, Suzana and Mitrić, M. and Pavlović, Vladimir and Nikolić, P.M. and Djordjević, Antonije and Ristić, M.M.", year = "2012", abstract = "Mixtures of BaCO3, ZnO and TiO2 powders, with molar ratio of 1:2:4, were mechanically activated for 20, 40 and minutes in a planetary ball mill. The resulting powders were compacted into pellets and isothermally sintered at 1250 degrees C for 2h with a heating rate of 10 degrees C/min. X-ray diffraction analysis of obtained powders and sintered samples was performed in order to investigate changes of the phase composition. The microstructure of sintered samples was examined by scanning electron microscopy. The photoacoustic phase and amplitude spectra of sintered samples were measured as a function of the laser beam modulating frequency using a transmission detection configuration. Fitting of experimental data enabled determination of photoacoustic properties including thermal diffusivity. Based on the results obtained correlation between thermal diffusivity and experimental conditions, as well the samples microstructure characteristics, was discussed.", publisher = "Međunarodni Institut za nauku o sinterovanju, Beograd", journal = "Science of Sintering", title = "Synthesis of Barium-zinc-titanate Ceramics", pages = "71-65", number = "1", volume = "44", doi = "10.2298/SOS1201065O" }
Obradović, N., Nikolić, M.V., Nikolić, N., Filipović, S., Mitrić, M., Pavlović, V., Nikolić, P.M., Djordjević, A.,& Ristić, M.M.. (2012). Synthesis of Barium-zinc-titanate Ceramics. in Science of Sintering Međunarodni Institut za nauku o sinterovanju, Beograd., 44(1), 65-71. https://doi.org/10.2298/SOS1201065O
Obradović N, Nikolić M, Nikolić N, Filipović S, Mitrić M, Pavlović V, Nikolić P, Djordjević A, Ristić M. Synthesis of Barium-zinc-titanate Ceramics. in Science of Sintering. 2012;44(1):65-71. doi:10.2298/SOS1201065O .
Obradović, N., Nikolić, M.V., Nikolić, N., Filipović, Suzana, Mitrić, M., Pavlović, Vladimir, Nikolić, P.M., Djordjević, Antonije, Ristić, M.M., "Synthesis of Barium-zinc-titanate Ceramics" in Science of Sintering, 44, no. 1 (2012):65-71, https://doi.org/10.2298/SOS1201065O . .