Characterisation of Mn0.63Zn0.37Fe2O4 Powders After Intensive Milling and Subsequent Thermal Treatment
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes ...
Sintering of Fly Ash Based Composites with Zeolite and Bentonite Addition for Application in Construction Materials
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Due to pozzolanic characteristics, fly ash is commonly used as a cement replacement in construction composites. Addition of natural clays with sorption ability (i.e. zeolite and bentonite) in to the fly ash based construction ...
Formation of Porous Wollastonite-based Ceramics after Sintering With Yeast as the Pore-forming Agent
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
In this paper, synthesis of porous wollastonite-based ceramics was reported. Ceramic precursor, methylhydrocyclosiloxane, together with micro-sized CaCO3, was used as starting material. After 20 min of ultrasound treatment, ...