The influence of mechanical activation on the electrical properties of Ba0.77Sr0.23TiO3
(2013)
Poster presented at the conference Advanced Ceramics and Application II – Serbian Ceramic Society, Belgrade, September 30 – October 1, 2013
Density and electrical properties of cordierite based ceramics as function of compaction pressure
(Belgrade : Serbian Ceramic Society, 2013)
Mechanical activation is widely used and relatively inexpensive procedure for sintering process sample preparation. However, the influence of pressure, which is used for compaction, has not been completely investigated. ...
The Morphological Characterization of Mechanically Activated ZnO Powder
(Belgrade : Serbian Ceramic Society, 2014)
The authors investigated the morphological characteristics of mechanically activated ZnO powder. ZnO powder was mechanically activated for 2, 5, 10 and 30 minutes in a planetary ball mill. Mechanical activation introduces ...
The influence of mechanical activation on the electrical properties of Ba0.77Sr0.23TiO3 ceramics
(Belgrade : Serbian Ceramic Society, 2013)
Ferroelectric ceramic barium strontium titanate (Ba0.77Sr0.23TiO3), BST, was prepared by solid-state reactions using starting powders of barium carbonate (BaCO3), strontium carbonate (SrCO3) and titanium dioxide (TiO2-anatase). ...
Characterization of mechanically activated ZnO powder
(Belgrade : Serbian Ceramic Society, 2013)
Materials based on ZnO structure have more frequently application as fillers in polymer ceramics nanocompozites. Performances of these materials depends on fillers morphology, surfaces texture and particles size. According ...
Dilatometric Analysis of Mechanically Activated SrTiO3 Powder
(Belgrade : Serbian Ceramic Society, 2013)
Strontium-titanate powder was mechanically activated in a planetary ball mill for 0, 5, 10, 30, 60, 90 and 120 minutes. Non-isothermal sintering of non-activated and activated SrTiO3 powder samples in the temperature ...
The effect of Hot Isostatic Pressing on the MT sample densities
(Belgrade : Serbian Ceramic Society, 2015)
Mechanically activated powders (0, 10, 40, 80 and 160 minutes) were formed by isostatic pressure 300 MPa to cylindrical green bodies (φ 12 mm). First set of samples was sintered at 1300°C for 30 min in air (heating rate ...
Structural characterization of mechanically activated MgO-TiO2 system
(Belgrade : Serbian Ceramic Society, 2013)
In this article the influence of ball miling process on structure of MgO-TiO2 system was investigated. The mixtures of MgO-TiO2 powders were mechanically activated in a planetary ball mill for the time period from 0 to 120 ...