TY  - CONF
AU  - Obradović, Nina
AU  - Fahrenholtz, William G.
AU  - Filipović, Suzana
AU  - Đorđević, Pavle
AU  - Rogan, Jelena
AU  - Pavlović, Vladimir
PY  - 2019
UR  - http://dais.sanu.ac.rs/123456789/7050
UR  - http://aspace.agrif.bg.ac.rs/handle/123456789/5757
AB  - Magnesium aluminate and other alumina-based spinels attract attention due to their high hardness, high mechanical strength, and low dielectric constant. MgAl2O4 was produced by solid-state reaction between MgO and a-Al2O3 powders. Mechanical activation was used to increase the reactivity of powders and decrease the sintering temperatures. Mechanical activation of mixed powders was performed in a high-energy planetary ball mill in air for 30, 60, 90, and 120 minutes. The resulting powders were characterized to determine the effect of activation on surface area, particle size, and crystallinity. Mechanical activation decreased particle size, increased surface area, and increased the width of peaks in x-ray diffraction. Dilatometry was used to monitor densification behavior up to 1500 °C. For non-activated powders, sintering started at approximately 1400 °C, while for activated powders, the onset temperature decreased to about 1340 °C. Mechanical activation is an efficient method to improve the densification behaviour of MgAl2O4 produced from mixed oxide powders.
PB  - The Ceramic Society of Japan
C3  - The 13th Pacific Rim Conference of Ceramic Societies (PACRIM13), October 27 - November 1, 2019, Okinawa Convention Center, Japan
T1  - Effect of Mechanical Activation on the Densification Behavior of MgAl2O4 Spinel
SP  - 30-B1C-S13-14
UR  - https://hdl.handle.net/21.15107/rcub_dais_7050
ER  - 

@conference{
author = "Obradović, Nina and Fahrenholtz, William G. and Filipović, Suzana and Đorđević, Pavle and Rogan, Jelena and Pavlović, Vladimir",
year = "2019",
abstract = "Magnesium aluminate and other alumina-based spinels attract attention due to their high hardness, high mechanical strength, and low dielectric constant. MgAl2O4 was produced by solid-state reaction between MgO and a-Al2O3 powders. Mechanical activation was used to increase the reactivity of powders and decrease the sintering temperatures. Mechanical activation of mixed powders was performed in a high-energy planetary ball mill in air for 30, 60, 90, and 120 minutes. The resulting powders were characterized to determine the effect of activation on surface area, particle size, and crystallinity. Mechanical activation decreased particle size, increased surface area, and increased the width of peaks in x-ray diffraction. Dilatometry was used to monitor densification behavior up to 1500 °C. For non-activated powders, sintering started at approximately 1400 °C, while for activated powders, the onset temperature decreased to about 1340 °C. Mechanical activation is an efficient method to improve the densification behaviour of MgAl2O4 produced from mixed oxide powders.",
publisher = "The Ceramic Society of Japan",
journal = "The 13th Pacific Rim Conference of Ceramic Societies (PACRIM13), October 27 - November 1, 2019, Okinawa Convention Center, Japan",
title = "Effect of Mechanical Activation on the Densification Behavior of MgAl2O4 Spinel",
pages = "30-B1C-S13-14",
url = "https://hdl.handle.net/21.15107/rcub_dais_7050"
}

Obradović, N., Fahrenholtz, W. G., Filipović, S., Đorđević, P., Rogan, J.,& Pavlović, V.. (2019). Effect of Mechanical Activation on the Densification Behavior of MgAl2O4 Spinel. in The 13th Pacific Rim Conference of Ceramic Societies (PACRIM13), October 27 - November 1, 2019, Okinawa Convention Center, Japan
The Ceramic Society of Japan., 30-B1C-S13-14.
https://hdl.handle.net/21.15107/rcub_dais_7050

Obradović N, Fahrenholtz WG, Filipović S, Đorđević P, Rogan J, Pavlović V. Effect of Mechanical Activation on the Densification Behavior of MgAl2O4 Spinel. in The 13th Pacific Rim Conference of Ceramic Societies (PACRIM13), October 27 - November 1, 2019, Okinawa Convention Center, Japan. 2019;:30-B1C-S13-14.
https://hdl.handle.net/21.15107/rcub_dais_7050 .

Obradović, Nina, Fahrenholtz, William G., Filipović, Suzana, Đorđević, Pavle, Rogan, Jelena, Pavlović, Vladimir, "Effect of Mechanical Activation on the Densification Behavior of MgAl2O4 Spinel" in The 13th Pacific Rim Conference of Ceramic Societies (PACRIM13), October 27 - November 1, 2019, Okinawa Convention Center, Japan (2019):30-B1C-S13-14,
https://hdl.handle.net/21.15107/rcub_dais_7050 .

TY  - CONF
AU  - Obradović, Nina
AU  - Fahrenholtz, William G.
AU  - Filipović, Suzana
AU  - Đorđević, Pavle
AU  - Marković, Smilja
AU  - Rogan, Jelena
AU  - Vulić, Predrag J.
AU  - Pavlović, Vladimir
PY  - 2019
UR  - http://dais.sanu.ac.rs/123456789/6980
UR  - http://aspace.agrif.bg.ac.rs/handle/123456789/5748
AB  - Single crystalline phase MgAl2O4 is made from the predetermined composition of MgO-Al2O3 powder mixture by using ball-milling. Mixtures of MgO and Al2O3 are treated in planetary ball mill for 30, 60, 90 and 120 minutes, in air. The aim of this experiment was to examine phase composition, microstructure, and densification behavior of all sintered samples and to find out which sample has the best features for further use. After sintering in dilatometer at 1500 °C, XRD patterns and SEM images were recorded. The results show that mechanical activation is an efficient method to improve the densification behavior of MgAl2O4 sintered specimens. With the prolonged milling time, densities increased, reaching the maximum value of 2.8 g/cm3 for sample activated 120 minutes.
PB  - Belgrade : Serbian Ceramic Society
C3  - Program and the Book of abstracts / Serbian Ceramic Society Conference Advanced Ceramics and Application VIII : New Frontiers in Multifunctional Material Science and Processing, Serbia, Belgrade, 23-25. September 2019
T1  - Characterization of MgAl2O4 sintered ceramics
EP  - 54
SP  - 54
UR  - https://hdl.handle.net/21.15107/rcub_dais_6980
ER  - 

@conference{
author = "Obradović, Nina and Fahrenholtz, William G. and Filipović, Suzana and Đorđević, Pavle and Marković, Smilja and Rogan, Jelena and Vulić, Predrag J. and Pavlović, Vladimir",
year = "2019",
abstract = "Single crystalline phase MgAl2O4 is made from the predetermined composition of MgO-Al2O3 powder mixture by using ball-milling. Mixtures of MgO and Al2O3 are treated in planetary ball mill for 30, 60, 90 and 120 minutes, in air. The aim of this experiment was to examine phase composition, microstructure, and densification behavior of all sintered samples and to find out which sample has the best features for further use. After sintering in dilatometer at 1500 °C, XRD patterns and SEM images were recorded. The results show that mechanical activation is an efficient method to improve the densification behavior of MgAl2O4 sintered specimens. With the prolonged milling time, densities increased, reaching the maximum value of 2.8 g/cm3 for sample activated 120 minutes.",
publisher = "Belgrade : Serbian Ceramic Society",
journal = "Program and the Book of abstracts / Serbian Ceramic Society Conference Advanced Ceramics and Application VIII : New Frontiers in Multifunctional Material Science and Processing, Serbia, Belgrade, 23-25. September 2019",
title = "Characterization of MgAl2O4 sintered ceramics",
pages = "54-54",
url = "https://hdl.handle.net/21.15107/rcub_dais_6980"
}

Obradović, N., Fahrenholtz, W. G., Filipović, S., Đorđević, P., Marković, S., Rogan, J., Vulić, P. J.,& Pavlović, V.. (2019). Characterization of MgAl2O4 sintered ceramics. in Program and the Book of abstracts / Serbian Ceramic Society Conference Advanced Ceramics and Application VIII : New Frontiers in Multifunctional Material Science and Processing, Serbia, Belgrade, 23-25. September 2019
Belgrade : Serbian Ceramic Society., 54-54.
https://hdl.handle.net/21.15107/rcub_dais_6980

Obradović N, Fahrenholtz WG, Filipović S, Đorđević P, Marković S, Rogan J, Vulić PJ, Pavlović V. Characterization of MgAl2O4 sintered ceramics. in Program and the Book of abstracts / Serbian Ceramic Society Conference Advanced Ceramics and Application VIII : New Frontiers in Multifunctional Material Science and Processing, Serbia, Belgrade, 23-25. September 2019. 2019;:54-54.
https://hdl.handle.net/21.15107/rcub_dais_6980 .

Obradović, Nina, Fahrenholtz, William G., Filipović, Suzana, Đorđević, Pavle, Marković, Smilja, Rogan, Jelena, Vulić, Predrag J., Pavlović, Vladimir, "Characterization of MgAl2O4 sintered ceramics" in Program and the Book of abstracts / Serbian Ceramic Society Conference Advanced Ceramics and Application VIII : New Frontiers in Multifunctional Material Science and Processing, Serbia, Belgrade, 23-25. September 2019 (2019):54-54,
https://hdl.handle.net/21.15107/rcub_dais_6980 .