AB  - In this article the influence of ball miling process on structure of MgO-TiO2 system was investigated. The mixtures of MgO-TiO2 powders were mechanically activated in a planetary ball mill for the time period from 0 to 120 minutes. The influence of mechanical activation on the lattice vibrational spectra was studied by Raman spectroscopy at room temperature. Structural investigations have been performed on produced powders. Nitrogen adsorption method was used to determine the BET specific surface area and pore size distribution. Unusual results have been obtained: specific surface area continuously decreased up to 40 minutes of activation and increased after that, reaching its minimun value of 5.5 m2/g. The Raman spectra of activated powders have shown that anatase modes have been decreasing in intensity and broadening as the time of activation extended. Also, the additional modes attributed to TiO2 II, srilankite and rutile phases started to appear as a consequence of activation.
PB  - Belgrade : Serbian Ceramic Society
C3  - Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts : II Serbian Ceramic Society Conference, Sep 30th-Oct 1st, 2013, Belgrade
T1  - Structural characterization of mechanically activated MgO-TiO2 system
EP  - 41
SP  - 40
UR  - https://hdl.handle.net/21.15107/rcub_dais_418
ER  - 

@conference{
author = "Filipović, Suzana and Obradović, Nina and Šćepanović, M. and Pavlović, Vladimir B. and Ristić, Momčilo M.",
year = "2013",
abstract = "In this article the influence of ball miling process on structure of MgO-TiO2 system was investigated. The mixtures of MgO-TiO2 powders were mechanically activated in a planetary ball mill for the time period from 0 to 120 minutes. The influence of mechanical activation on the lattice vibrational spectra was studied by Raman spectroscopy at room temperature. Structural investigations have been performed on produced powders. Nitrogen adsorption method was used to determine the BET specific surface area and pore size distribution. Unusual results have been obtained: specific surface area continuously decreased up to 40 minutes of activation and increased after that, reaching its minimun value of 5.5 m2/g. The Raman spectra of activated powders have shown that anatase modes have been decreasing in intensity and broadening as the time of activation extended. Also, the additional modes attributed to TiO2 II, srilankite and rutile phases started to appear as a consequence of activation.",
publisher = "Belgrade : Serbian Ceramic Society",
journal = "Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts : II Serbian Ceramic Society Conference, Sep 30th-Oct 1st, 2013, Belgrade",
title = "Structural characterization of mechanically activated MgO-TiO2 system",
pages = "41-40",
url = "https://hdl.handle.net/21.15107/rcub_dais_418"
}

Filipović, S., Obradović, N., Šćepanović, M., Pavlović, V. B.,& Ristić, M. M.. (2013). Structural characterization of mechanically activated MgO-TiO2 system. in Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts : II Serbian Ceramic Society Conference, Sep 30th-Oct 1st, 2013, Belgrade
Belgrade : Serbian Ceramic Society., 40-41.
https://hdl.handle.net/21.15107/rcub_dais_418

Filipović S, Obradović N, Šćepanović M, Pavlović VB, Ristić MM. Structural characterization of mechanically activated MgO-TiO2 system. in Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts : II Serbian Ceramic Society Conference, Sep 30th-Oct 1st, 2013, Belgrade. 2013;:40-41.
https://hdl.handle.net/21.15107/rcub_dais_418 .

Filipović, Suzana, Obradović, Nina, Šćepanović, M., Pavlović, Vladimir B., Ristić, Momčilo M., "Structural characterization of mechanically activated MgO-TiO2 system" in Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts : II Serbian Ceramic Society Conference, Sep 30th-Oct 1st, 2013, Belgrade (2013):40-41,
https://hdl.handle.net/21.15107/rcub_dais_418 .

TY  - CONF
AU  - Filipović, Suzana
AU  - Obradović, Nina
AU  - Krstić, Jugoslav
AU  - Šćepanović, M.
AU  - Pavlović, Vladimir B.
AU  - Paunović, Vesna
AU  - Ristić, Momčilo M.
PY  - 2012
UR  - http://dais.sanu.ac.rs/123456789/442
UR  - http://aspace.agrif.bg.ac.rs/handle/123456789/5682
AB  - In this article the influence of ball milling process on structure of MgO-TiO2 system, along with its influence on electrical properties of post-sintering samples, were investigated. Mixtures of MgO-TiO2 powders were mechanically activated in a planetary ball mill for time interval from 0 to 120 minutes. On thus obtained powders, structural investigations have been performed. N2 adsorption method was used to determine the BET specific surface area and pore size distribution. Unusual results were obtained: specific surface area continuously decreases up to 40 minutes of activation and after that increases, reaching its minimum value of 5.5 m2/g. The influence of mechanical activation on lattice vibration spectra was examined by Raman spectroscopy at room temperature. For sintered samples characterization, Raman scattering spectroscopy has been used. Very similar spectra for all samples were observed. Raman spectroscopy of sintered samples indicates a presence of two phases, while varieties in spectra were explained with different ratio of present phases. Effect of activation and sintering process on microstructure was investigated by scanning electron microscopy (SEM). Electrical measurements showed difference in dielectric constant (εr), loss tangent (tgδ) and specific resistance (ρ) as a function of time of mechanical treatment.
PB  - Belgrade : Materials Research Society of Serbia
C3  - The Fourteenth Annual Conference YUCOMAT 2012: Programme and the Book of Abstracts
T1  - Structural characterization and electrical properties of sintered magnesium-titanate ceramics
EP  - 80
SP  - 80
UR  - https://hdl.handle.net/21.15107/rcub_dais_442
ER  - 

@conference{
author = "Filipović, Suzana and Obradović, Nina and Krstić, Jugoslav and Šćepanović, M. and Pavlović, Vladimir B. and Paunović, Vesna and Ristić, Momčilo M.",
year = "2012",
abstract = "In this article the influence of ball milling process on structure of MgO-TiO2 system, along with its influence on electrical properties of post-sintering samples, were investigated. Mixtures of MgO-TiO2 powders were mechanically activated in a planetary ball mill for time interval from 0 to 120 minutes. On thus obtained powders, structural investigations have been performed. N2 adsorption method was used to determine the BET specific surface area and pore size distribution. Unusual results were obtained: specific surface area continuously decreases up to 40 minutes of activation and after that increases, reaching its minimum value of 5.5 m2/g. The influence of mechanical activation on lattice vibration spectra was examined by Raman spectroscopy at room temperature. For sintered samples characterization, Raman scattering spectroscopy has been used. Very similar spectra for all samples were observed. Raman spectroscopy of sintered samples indicates a presence of two phases, while varieties in spectra were explained with different ratio of present phases. Effect of activation and sintering process on microstructure was investigated by scanning electron microscopy (SEM). Electrical measurements showed difference in dielectric constant (εr), loss tangent (tgδ) and specific resistance (ρ) as a function of time of mechanical treatment.",
publisher = "Belgrade : Materials Research Society of Serbia",
journal = "The Fourteenth Annual Conference YUCOMAT 2012: Programme and the Book of Abstracts",
title = "Structural characterization and electrical properties of sintered magnesium-titanate ceramics",
pages = "80-80",
url = "https://hdl.handle.net/21.15107/rcub_dais_442"
}

Filipović, S., Obradović, N., Krstić, J., Šćepanović, M., Pavlović, V. B., Paunović, V.,& Ristić, M. M.. (2012). Structural characterization and electrical properties of sintered magnesium-titanate ceramics. in The Fourteenth Annual Conference YUCOMAT 2012: Programme and the Book of Abstracts
Belgrade : Materials Research Society of Serbia., 80-80.
https://hdl.handle.net/21.15107/rcub_dais_442

Filipović S, Obradović N, Krstić J, Šćepanović M, Pavlović VB, Paunović V, Ristić MM. Structural characterization and electrical properties of sintered magnesium-titanate ceramics. in The Fourteenth Annual Conference YUCOMAT 2012: Programme and the Book of Abstracts. 2012;:80-80.
https://hdl.handle.net/21.15107/rcub_dais_442 .

Filipović, Suzana, Obradović, Nina, Krstić, Jugoslav, Šćepanović, M., Pavlović, Vladimir B., Paunović, Vesna, Ristić, Momčilo M., "Structural characterization and electrical properties of sintered magnesium-titanate ceramics" in The Fourteenth Annual Conference YUCOMAT 2012: Programme and the Book of Abstracts (2012):80-80,
https://hdl.handle.net/21.15107/rcub_dais_442 .