TY  - JOUR
AU  - Nikolić, Nebojša D.
AU  - Avramović, Ljiljana
AU  - Ivanović, Evica
AU  - Maksimović, Vesna M.
AU  - Baščarević, Zvezdana
AU  - Ignjatović, Nenad
PY  - 2019
UR  - http://aspace.agrif.bg.ac.rs/handle/123456789/5048
AB  - Production of copper powders by the potentiostatic electrolysis under different hydrogen evolution conditions was investigated. Copper powders were characterized by the scanning electron microscope (SEM), X-ray diffraction (XRD), particle size distribution (PSD), and by the determination of the specific surface area (SSA) of the formed powders. Depending on quantity of hydrogen generated during electrolysis, the two types of particles were formed: dendrites and cauliflower-like particles. The dendrites were formed without, while cauliflower-like particles with the quantity of evolved hydrogen enough to achieve strong effect on hydrodynamic conditions in the near-electrode layer. Although macro structure of the particles was very different, they showed similar micro structure. Namely, both types of the particles consisted of small agglomerates of approximately spherical Cu grains at the micro level. The existence of the spherical morphology was just responsible for random orientation of Cu crystallites in both types of particles. The SSA of cauliflower-like particles was more than two times larger than that of the dendrites, while their size was considerably smaller than that of the dendritic particles. In this way, the useful benefit of Cu powder formation in the conditions of vigorous hydrogen evolution is shown.
PB  - Elsevier Science Bv, Amsterdam
T2  - Transactions of Nonferrous Metals Society of China
T1  - Comparative morphological and crystallographic analysis of copper powders obtained under different electrolysis conditions
EP  - 1284
IS  - 6
SP  - 1275
VL  - 29
DO  - 10.1016/S1003-6326(19)65034-X
ER  - 

@article{
author = "Nikolić, Nebojša D. and Avramović, Ljiljana and Ivanović, Evica and Maksimović, Vesna M. and Baščarević, Zvezdana and Ignjatović, Nenad",
year = "2019",
abstract = "Production of copper powders by the potentiostatic electrolysis under different hydrogen evolution conditions was investigated. Copper powders were characterized by the scanning electron microscope (SEM), X-ray diffraction (XRD), particle size distribution (PSD), and by the determination of the specific surface area (SSA) of the formed powders. Depending on quantity of hydrogen generated during electrolysis, the two types of particles were formed: dendrites and cauliflower-like particles. The dendrites were formed without, while cauliflower-like particles with the quantity of evolved hydrogen enough to achieve strong effect on hydrodynamic conditions in the near-electrode layer. Although macro structure of the particles was very different, they showed similar micro structure. Namely, both types of the particles consisted of small agglomerates of approximately spherical Cu grains at the micro level. The existence of the spherical morphology was just responsible for random orientation of Cu crystallites in both types of particles. The SSA of cauliflower-like particles was more than two times larger than that of the dendrites, while their size was considerably smaller than that of the dendritic particles. In this way, the useful benefit of Cu powder formation in the conditions of vigorous hydrogen evolution is shown.",
publisher = "Elsevier Science Bv, Amsterdam",
journal = "Transactions of Nonferrous Metals Society of China",
title = "Comparative morphological and crystallographic analysis of copper powders obtained under different electrolysis conditions",
pages = "1284-1275",
number = "6",
volume = "29",
doi = "10.1016/S1003-6326(19)65034-X"
}

Nikolić, N. D., Avramović, L., Ivanović, E., Maksimović, V. M., Baščarević, Z.,& Ignjatović, N.. (2019). Comparative morphological and crystallographic analysis of copper powders obtained under different electrolysis conditions. in Transactions of Nonferrous Metals Society of China
Elsevier Science Bv, Amsterdam., 29(6), 1275-1284.
https://doi.org/10.1016/S1003-6326(19)65034-X

Nikolić ND, Avramović L, Ivanović E, Maksimović VM, Baščarević Z, Ignjatović N. Comparative morphological and crystallographic analysis of copper powders obtained under different electrolysis conditions. in Transactions of Nonferrous Metals Society of China. 2019;29(6):1275-1284.
doi:10.1016/S1003-6326(19)65034-X .

Nikolić, Nebojša D., Avramović, Ljiljana, Ivanović, Evica, Maksimović, Vesna M., Baščarević, Zvezdana, Ignjatović, Nenad, "Comparative morphological and crystallographic analysis of copper powders obtained under different electrolysis conditions" in Transactions of Nonferrous Metals Society of China, 29, no. 6 (2019):1275-1284,
https://doi.org/10.1016/S1003-6326(19)65034-X . .

TY  - JOUR
AU  - Avramović, Ljiljana
AU  - Ivanović, Evica
AU  - Maksimović, Vesna M.
AU  - Pavlović, Miroslav M.
AU  - Vuković, Marina
AU  - Stevanović, Jasmina S.
AU  - Nikolić, Nebojša D.
PY  - 2018
UR  - http://aspace.agrif.bg.ac.rs/handle/123456789/4641
AB  - Silver dendritic nanonstructures obtained by the potentiostatic electrolysis from different electrolytes at different overpotentials were characterized by the scanning electron microscopy (SEM) technique and X-ray diffraction analysis of the produced particles. The needle-like and fern-like dendrites were formed from the nitrate electrolyte at overpotentials inside and outside plateaus of the limiting diffusion current density, respectively. The three-dimensional pine-like dendrites constructed from approximately spherical grains were formed from the ammonium electrolyte at overpotentials both inside and outside plateaus of the limiting diffusion current density. The morphology of silver dendrites was correlated with their crystal structure at the semi quantiative level. The change of crystal orientation from the strong (111) preferred orientation for the needle-like dendrites to almost randomly orientied spherical grains in the pine-like dendrites obtained at the overpotential outside the plateau of the limiting diffusion current density was observed. This trend in change of crystal orientation and morphology of Ag nanostructures was accompanied by considerable increase of the specific surface area (SSA) of the produced powders. The average crystallite sizes were in the range of 38-50 nm, proving nanostructural character of the formed Ag particles.
PB  - Elsevier Science Bv, Amsterdam
T2  - Transactions of Nonferrous Metals Society of China
T1  - Correlation between crystal structure and morphology of potentiostatically electrodeposited silver dendritic nanostructures
EP  - 1912
IS  - 9
SP  - 1903
VL  - 28
DO  - 10.1016/S1003-6326(18)64835-6
ER  - 

@article{
author = "Avramović, Ljiljana and Ivanović, Evica and Maksimović, Vesna M. and Pavlović, Miroslav M. and Vuković, Marina and Stevanović, Jasmina S. and Nikolić, Nebojša D.",
year = "2018",
abstract = "Silver dendritic nanonstructures obtained by the potentiostatic electrolysis from different electrolytes at different overpotentials were characterized by the scanning electron microscopy (SEM) technique and X-ray diffraction analysis of the produced particles. The needle-like and fern-like dendrites were formed from the nitrate electrolyte at overpotentials inside and outside plateaus of the limiting diffusion current density, respectively. The three-dimensional pine-like dendrites constructed from approximately spherical grains were formed from the ammonium electrolyte at overpotentials both inside and outside plateaus of the limiting diffusion current density. The morphology of silver dendrites was correlated with their crystal structure at the semi quantiative level. The change of crystal orientation from the strong (111) preferred orientation for the needle-like dendrites to almost randomly orientied spherical grains in the pine-like dendrites obtained at the overpotential outside the plateau of the limiting diffusion current density was observed. This trend in change of crystal orientation and morphology of Ag nanostructures was accompanied by considerable increase of the specific surface area (SSA) of the produced powders. The average crystallite sizes were in the range of 38-50 nm, proving nanostructural character of the formed Ag particles.",
publisher = "Elsevier Science Bv, Amsterdam",
journal = "Transactions of Nonferrous Metals Society of China",
title = "Correlation between crystal structure and morphology of potentiostatically electrodeposited silver dendritic nanostructures",
pages = "1912-1903",
number = "9",
volume = "28",
doi = "10.1016/S1003-6326(18)64835-6"
}

Avramović, L., Ivanović, E., Maksimović, V. M., Pavlović, M. M., Vuković, M., Stevanović, J. S.,& Nikolić, N. D.. (2018). Correlation between crystal structure and morphology of potentiostatically electrodeposited silver dendritic nanostructures. in Transactions of Nonferrous Metals Society of China
Elsevier Science Bv, Amsterdam., 28(9), 1903-1912.
https://doi.org/10.1016/S1003-6326(18)64835-6

Avramović L, Ivanović E, Maksimović VM, Pavlović MM, Vuković M, Stevanović JS, Nikolić ND. Correlation between crystal structure and morphology of potentiostatically electrodeposited silver dendritic nanostructures. in Transactions of Nonferrous Metals Society of China. 2018;28(9):1903-1912.
doi:10.1016/S1003-6326(18)64835-6 .

Avramović, Ljiljana, Ivanović, Evica, Maksimović, Vesna M., Pavlović, Miroslav M., Vuković, Marina, Stevanović, Jasmina S., Nikolić, Nebojša D., "Correlation between crystal structure and morphology of potentiostatically electrodeposited silver dendritic nanostructures" in Transactions of Nonferrous Metals Society of China, 28, no. 9 (2018):1903-1912,
https://doi.org/10.1016/S1003-6326(18)64835-6 . .