Апстракт
Barium-titanate powder was mechanically activated in a planetary-ball mill for 60 and 120 minutes. Non-isothermal sintering of non-activated and activated powder samples was investigated using a dilatometer in the temperature interval from room to 1380oC with three different heating rates (10, 20 and 30oC/min). Early-stage sintering mechanisms for all three types of samples were analyzed, showing significant differences between the non-activated and mechanically activated samples.
Prah barijum-titanata je mehanički aktiviran u planetarnom mlinu sa kuglicama 60 i 120 minuta. Neizotermsko sinterovanje neaktiviranog i aktiviranih uzoraka proučeno je u dilatometru u temperaturskom intervalu od sobne do 1380oS sa tri različite brzine zagrevanja (10, 20 i 30oS/min). Mehanizmi ranih stadijuma sinterovanja su analizirani za sva tri tipa uzoraka i uočene su značajne razlike između neaktiviranih i mehanički aktiviranih uzoraka.
Кључне речи:
BaTiO3 / mechanical activation / sintering mechanism / BaTiO3 / mehanička aktivacija / mehanizam sinterovanjaИзвор:
Science of Sintering, 2006, 38, 3, 239-244Издавач:
- Međunarodni Institut za nauku o sinterovanju, Beograd
DOI: 10.2298/SOS0603239N
ISSN: 0350-820X
WoS: 000243986800006
Scopus: 2-s2.0-66149180464
Институција/група
Poljoprivredni fakultetTY - JOUR AU - Nikolić, M.V. AU - Pavlović, Vera P. AU - Pavlović, Vladimir AU - Ristić, M.M. PY - 2006 UR - http://aspace.agrif.bg.ac.rs/handle/123456789/1337 AB - Barium-titanate powder was mechanically activated in a planetary-ball mill for 60 and 120 minutes. Non-isothermal sintering of non-activated and activated powder samples was investigated using a dilatometer in the temperature interval from room to 1380oC with three different heating rates (10, 20 and 30oC/min). Early-stage sintering mechanisms for all three types of samples were analyzed, showing significant differences between the non-activated and mechanically activated samples. AB - Prah barijum-titanata je mehanički aktiviran u planetarnom mlinu sa kuglicama 60 i 120 minuta. Neizotermsko sinterovanje neaktiviranog i aktiviranih uzoraka proučeno je u dilatometru u temperaturskom intervalu od sobne do 1380oS sa tri različite brzine zagrevanja (10, 20 i 30oS/min). Mehanizmi ranih stadijuma sinterovanja su analizirani za sva tri tipa uzoraka i uočene su značajne razlike između neaktiviranih i mehanički aktiviranih uzoraka. PB - Međunarodni Institut za nauku o sinterovanju, Beograd T2 - Science of Sintering T1 - Analysis of early-stage sintering mechanisms of mechanically activated BaTiO3 EP - 244 IS - 3 SP - 239 VL - 38 DO - 10.2298/SOS0603239N ER -
@article{ author = "Nikolić, M.V. and Pavlović, Vera P. and Pavlović, Vladimir and Ristić, M.M.", year = "2006", abstract = "Barium-titanate powder was mechanically activated in a planetary-ball mill for 60 and 120 minutes. Non-isothermal sintering of non-activated and activated powder samples was investigated using a dilatometer in the temperature interval from room to 1380oC with three different heating rates (10, 20 and 30oC/min). Early-stage sintering mechanisms for all three types of samples were analyzed, showing significant differences between the non-activated and mechanically activated samples., Prah barijum-titanata je mehanički aktiviran u planetarnom mlinu sa kuglicama 60 i 120 minuta. Neizotermsko sinterovanje neaktiviranog i aktiviranih uzoraka proučeno je u dilatometru u temperaturskom intervalu od sobne do 1380oS sa tri različite brzine zagrevanja (10, 20 i 30oS/min). Mehanizmi ranih stadijuma sinterovanja su analizirani za sva tri tipa uzoraka i uočene su značajne razlike između neaktiviranih i mehanički aktiviranih uzoraka.", publisher = "Međunarodni Institut za nauku o sinterovanju, Beograd", journal = "Science of Sintering", title = "Analysis of early-stage sintering mechanisms of mechanically activated BaTiO3", pages = "244-239", number = "3", volume = "38", doi = "10.2298/SOS0603239N" }
Nikolić, M.V., Pavlović, V. P., Pavlović, V.,& Ristić, M.M.. (2006). Analysis of early-stage sintering mechanisms of mechanically activated BaTiO3. in Science of Sintering Međunarodni Institut za nauku o sinterovanju, Beograd., 38(3), 239-244. https://doi.org/10.2298/SOS0603239N
Nikolić M, Pavlović VP, Pavlović V, Ristić M. Analysis of early-stage sintering mechanisms of mechanically activated BaTiO3. in Science of Sintering. 2006;38(3):239-244. doi:10.2298/SOS0603239N .
Nikolić, M.V., Pavlović, Vera P., Pavlović, Vladimir, Ristić, M.M., "Analysis of early-stage sintering mechanisms of mechanically activated BaTiO3" in Science of Sintering, 38, no. 3 (2006):239-244, https://doi.org/10.2298/SOS0603239N . .